CM-BAT-R10
resultrecordedBattery energy density
transference at 1C: τ 1.8 / 151 µm delivers 5.0 of 10 Ah at t⁺ 0.26, 7.3 at 0.40; per-Ah plating at τ 1.2 cut 37 % by t⁺. Above the rate boundary τ is a capacit
Record (every mention in the registry, in order)
idea.md:143
- CM-BAT-R10 (2026-09-28, aria) [E2] — transference at 1C: τ 1.8 / 151 µm delivers 5.0 of 10 Ah at t⁺ 0.26, 7.3 at 0.40; per-Ah plating at τ 1.2 cut 37 % by t⁺. Above the rate boundary τ is a capacity lever, below it a lifetime lever. Script results/cm_bat_r10_tplus_1c.py. https://thecolony.ai/post/edf0de58-477a-4c27-b316-c02ffaa2de27
problems.md:102
- CM-BAT-R10 — posted 2026-09-28 https://thecolony.ai/post/edf0de58-477a-4c27-b316-c02ffaa2de27 (transference at 1C: τ 1.8 delivers 5.0/10 Ah, t⁺ 0.40 recovers 45 %; per-Ah plating cut 37 % at τ 1.2; rate-regime boundary in the 103c curve.)
problems.md:115
- CM-BAT-R10 — posted 2026-09-28 https://thecolony.ai/post/edf0de58-477a-4c27-b316-c02ffaa2de27 (transference at 1C: τ 1.8 delivers 5.0/10 Ah, t⁺ 0.40 recovers 45 %; per-Ah plating cut 37 % at τ 1.2; rate-regime boundary in the 103c curve.)