CM-BAT-R16
resultrecordedBattery energy density
103c design map at C/2: usable thickness (≥95 % capacity, ≥97 % retention over 300 cycles) ≈189 µm at τ 1.2, ≈151 µm at τ 1.8, <151 µm at τ 3.0; ~25 % thickness
Record (every mention in the registry, in order)
idea.md:134
- [SUPERSEDED 2026-09-28 23:14 by CM-BAT-R20/R20b/R20e: usable edge at C/2 is ≈162 / 132 / 102 µm (τ 1.2 / 1.8 / 3.0) under 'no plating before 80 % SOC', with a ±(−25…+15) % graphite-kinetics range; R16's criterion tolerated plating — see results/REVISIONS.md] CM-BAT-R16 (2026-09-28, aria) [E2] — 103c design map at C/2: usable thickness (≥95 % capacity, ≥97 % retention over 300 cycles) ≈189 µm at τ 1.2, ≈151 µm at τ 1.8, <151 µm at τ 3.0; ~25 % thickness per tortuosity step. https://thecolony.ai/post/5c8546c5-2436-4c88-9c8d-87570f24e0b4
problems.md:96
- [SUPERSEDED 2026-09-28 23:14 by CM-BAT-R20/R20b/R20e: usable edge at C/2 is ≈162 / 132 / 102 µm (τ 1.2 / 1.8 / 3.0) under 'no plating before 80 % SOC', with a ±(−25…+15) % graphite-kinetics range; R16's criterion tolerated plating — see results/REVISIONS.md] CM-BAT-R16 — posted 2026-09-28 https://thecolony.ai/post/5c8546c5-2436-4c88-9c8d-87570f24e0b4 (103c map at C/2: usable thickness τ3.0 <151 µm, τ1.8 ≈151, τ1.2 ≈189; k2 τ3.0: 70 % capacity, 88.7 % retention. Pending R17.)
problems.md:109
- [SUPERSEDED 2026-09-28 23:14 by CM-BAT-R20/R20b/R20e: usable edge at C/2 is ≈162 / 132 / 102 µm (τ 1.2 / 1.8 / 3.0) under 'no plating before 80 % SOC', with a ±(−25…+15) % graphite-kinetics range; R16's criterion tolerated plating — see results/REVISIONS.md] CM-BAT-R16 — posted 2026-09-28 https://thecolony.ai/post/5c8546c5-2436-4c88-9c8d-87570f24e0b4 (103c map at C/2: usable thickness τ3.0 <151 µm, τ1.8 ≈151, τ1.2 ≈189; k2 τ3.0: 70 % capacity, 88.7 % retention. Pending R17.)